Fiberlogy Nylon PA12 Filament 1.75 mm, 1 kg

Fiberlogy Nylon PA12 is a professional engineering-grade 3D printing filament designed for functional parts, industrial components and demanding mechanical applications. Based on Polyamide 12 (PA12), this material offers an excellent balance of toughness, chemical resistance, wear resistance and thermal stability.

The filament maintains its mechanical properties across a wide temperature range and delivers exceptional durability with elongation at break exceeding 50%. This combination of strength and flexibility helps printed parts resist cracking, impact damage and long-term mechanical stress.

Engineering-Grade PA12 Material

• High mechanical strength
• Excellent impact resistance
• Outstanding wear resistance
• Long service life
• High durability under demanding conditions

Excellent Chemical Resistance

Fiberlogy Nylon PA12 is highly resistant to many industrial fluids and chemicals, making it suitable for automotive and engineering applications.

• Resistant to oils
• Resistant to greases
• Resistant to fuels
• Resistant to hydraulic fluids
• Resistant to salt water
• Resistant to many solvents

Outstanding Mechanical Properties

• Density: 1.01 g/cm³
• Tensile Strength: 45 MPa
• Tensile Modulus: 1400 MPa
• Elongation at Break: >50%
• Charpy Impact Strength: 12 kJ/m²

Its combination of toughness and flexibility makes it ideal for parts exposed to vibration, repeated loads and mechanical wear. :contentReference[oaicite:6]{index=6}

High Temperature Performance

• HDT @ 0.45 MPa: 135°C
• HDT @ 1.8 MPa: 55°C
• Vicat Softening Temperature: 145°C
• Suitable for demanding thermal environments

Easy Post-Processing

Printed parts can be machined using standard tools and finished according to application requirements.

• Can be painted
• Can be drilled
• Can be milled
• Can be sanded

Recommended Print Settings

• Nozzle temperature: 255–270°C
• Bed temperature: 110°C
• Cooling fan: 0–10%
• Drying conditions: 70°C for 4 hours
• Enclosed chamber recommended
• Adhesive recommended for improved bed adhesion

Applications

• Functional prototypes
• Industrial components
• Mechanical parts
• Automotive applications
• Wear-resistant components
• Machine housings
• Chemical-resistant parts
• Engineering projects

Technical Specifications

• Manufacturer: Fiberlogy
• Material: Nylon PA12 (Polyamide 12)
• Filament Diameter: 1.75 mm
• Net Weight: 1 kg
• Density: 1.01 g/cm³
• Printing Temperature: 255–270°C
• Bed Temperature: 110°C
• Enclosure Recommended: Yes